Welcome to Shandong Tengyi Metal Materials Co., Ltd.
ER308
Application: Used for the welding of 18-8,18-12 and 20-10 type austenitic stainless steels with a wide application to petrochemical engineering,pressure vessels,food machinery, medical machinery,chemical fertilizer equipment,textile machinery and nuclear reaction etc. Such as welding of 12Cr18Ni9,06Cr19Ni10 etc.materials.
Characteristics: This welding wire is 21%-10%Ni austenitic stainless steel welding wire with a stable welding arc and beautiful formation of weld,available for the all-positioning welding.
Chemical Composition Of Welding Wire:(Mass Fraction)
| Item | C | Mn | Si | Cr | Ni | Mo | P | S | Cu |
| Guarantee Value | ≤0.08 | 1.00-2.50 | ≤0.65 | 19.50-22.00 | 9.00-11.00 | ≤0.75 | ≤0.030 | ≤0.030 | ≤0.75 |
| Typical Value | 0.04 | 1.68 | 0.39 | 20.12 | 9.48 | 0.036 | 0.012 | 0.009 | 0.32 |
Mechanical Property of Deposited Metal
| Item | Tensile Strength Rm/MPa | Elongation A% |
| Guarantee Value | ≥550 | ≥25 |
| Typical Value | 603 | 40 |
Note On Usage:
1.MIG welding shield gas flow should be between 18-25L/min;The shield gas should apply Ar+2%O₂;If the wind speed is greater than 0.5m/s,it is required to take the wind-proof measures.
2.TIG welding shield gas flow requirement:If the welding current is between(15-200)A, the gas flow should be(5-14)L/min;If the welding current is between(200-320)A,the gas flow should be(14-24)L/min.The shield gas should apply pure Ar,and please take the wind-proof measures is the wind speed is greater than 1.0m/s;It is required to remove the impurities e.g. rust,oil contaminant,water etc.on welding workpiece prior to MIG/TIG welding;The above- mentioned welding parameters should be for reference only,users should develop the welding standards appropriate for the production according to their own specific conditions.