Welcome to Shandong Tengyi Metal Materials Co., Ltd.
ER308LSi
Application: Used for the welding of materials with atmosphere corrosion resistance e.g. railway locomotives,truck body etc.Such as the welding of materials e.g.022Cr19Ni10(S304L) stainless steel,TCS used for transportation trucks etc.
Characteristics: This welding wire is 21%Cr-10%Ni ultra-low carbon austenitic stainless steel welding wire with a stable welding arc.Its molten iron has a good fluidity due to adding Si with a more beautiful formation of weld,available for the all-positioning welding
Chemical Composition Of Welding Wire:(Mass Fraction)
| Item | C | Mn | Si | Cr | Ni | Mo | P | S | Cu |
| Guarantee Value | ≤0.030 | 1.00 -2.50 | 0.65 -1.00 | 19.50 -22.00 | 9.00 -11.00 | ≤0.75 | ≤0.030 | ≤0.030 | ≤0.75 |
| Typical Value | 0.021 | 2.08 | 0.72 | 19.85 | 10.52 | 0.032 | 0.018 | 0.011 | 0.015 |
Mechanical Property of Deposited Metal
| Item | Tensile Strength Rm/MPa | Elongation A% |
| Guarantee Value | ≥510 | ≥25 |
| Typical Value | 595 | 40 |
Note On Usage:
1.MIG welding shield gas flow should be between 18-25L/min;The shield gas should apply Ar+2%O₂;If the wind speed is greater than 0.5m/s,it is required to take the wind-proof measures.
2.TIG welding shield gas flow requirement:If the welding current is between(15-200)A, the gas flow should be(5-14)L/min;If the welding current is between(200-320)A,the gas flow should be(14-24)L/min.The shield gas should apply pure Ar,and please take the wind-proof measures is the wind speed is greater than 1.0m/s;It is required to remove the impurities e.g. rust,oil contaminant,water etc.on welding workpiece prior to MIG/TIG welding;The above- mentioned welding parameters should be for reference only,users should develop the welding standards appropriate for the production according to their own specific conditions.